The Effect of Fiber Length Variations on the Composite Fiber of Oil Palm Empty Bunches (OPEB) on Tensile Strength
Pengaruh Variasi Panjang Serat pada Komposit Serat Tandan Kosong Kelapa Sawit (TKKS) terhadap Kekuatan Tarik
-
(1) Reksi Dwi Cahyanto Universitas Muhammadiyah Kalimantan Timur
Indonesia
(2) * Agus Mujianto
Universitas Muhammadiyah Kalimantan Timur
Indonesia
(3) Binyamin Binyamin Universitas Muhammadiyah Kalimantan Timur
Indonesia
(4) Andi Nugroho Universitas Muhammadiyah Kalimantan Timur
Indonesia
(*) Corresponding Author
Abstract
Composite is a combination of materials formed from mixing between two or more of the forming materials. This research aims to determine the effect of variations in fiber length with lengths of 4cm, 6cm, and 8cm with a volume fraction of OPEFB fiber of 30% and NaOH alkaline immersion for 2 hours. The tests carried out were tensile testing using ASTM D3039 and bending testing using ASTM D7264. Based on the study's results with the 30% OPEFB fraction with the highest tensile strength yield, the 8cm fiber length of 13,33 MPa was achieved. Meanwhile, the lowest value was achieved with a length of 4cm of 3,2MPa.
Downloads
References
L. Agustina, U. Udiantoro, and A. Halim, “Karakteristik Serat Tandan Kosong Kelapa Sawit (TKKS) dengan Perlakuan Perebusan dan Pengukusan,” Ziraa’ah Majalah Ilmiah Pertanian, vol. 41, no. 1, pp. 97–102, 2016, doi: 10.31602/zmip.v41i1.324.
A. Azwar, “Study Perilaku Mekanik Komposit Berbasis Polyester Yang Diperkuat Dengan Partikel Serbuk Kayu Keras dan Lunak,” Jurnal Reaksi, vol. 7, no. 16, 2009. DOI: https://doi.org/10.30811/jstr.v7i2.114
T. A. Adlie et al., “Pengaruh Beban Tarik Terhadap Variasi Ukuran Serat Tandan Kosong Kelapa Sawit Terhadap Kekuatan Tarik Komposit Polymeric Foam,” Jurnal Umum Teknologi Terapan, vol. 5, no. 1, doi: https://doi.org/10.55377/jurutera.v5i01.708 .
B. Bakri, M. Iqbal, and M. Rifki, “ANALISIS VARIASI PANJANG SERAT TERHADAP KUAT TARIK DAN LENTUR PADA KOMPOSIT YANG DIPERKUAT SERAT Agave angustifolia Haw,” Jurnal MEKANIKAL UNTAD, vol. 3, no. 1, May 2012.
H. Darmadi and S. Safitri, “Analisa Pengembangan Variasi Bahan Papan Komposit Berbahan dasar Tandan Kosong Kelapa Sawit Diperkuat Polyurethane Terhadap Pengujian Tekan,” Ready Star, vol. 2, no. 1, pp. 117–121, Nov. 2019.
E. D. Sulistyowati, N. H. Sari, I. Yudhyadi, S. Sinarep, and T. Topan, “Pengaruh Panjang Serat Dan Fraksi Volume Terhadap Kekuatan Impact Dan Bending Material Komposit Polyester Fiber Glass Dan Polyester Pandan Wangi,” Dinamika Teknik Mesin, vol. 2, no. 1, pp. 15–27, Jan. 2012. DOI: https://doi.org/10.29303/d.v2i1.107
S. Habibie et al., “Serat Alam Sebagai Bahan Komposit Ramah Lingkungan, Suatu Kajian Pustaka,” Jurnal Inovasi dan Teknologi Material, vol. 2, no. 2, pp. 1–13, Dec. 2021, doi: 10.29122/jitm.v2i2.4339.
S. Sunaryo, L. Hakim, Y. Yuhelson, and J. Japri, “Analisa Kinerja Alat Pengasap Ikan Salai Berbahan Bakar Tandan Kosong Kelapa Sawit,” Turbo : Jurnal Program Studi Teknik Mesin, vol. 11, no. 1, Jun. 2022, doi: 10.24127/trb.v11i1.1805. DOI: https://doi.org/10.24127/trb.v11i1.1805
S. Safrijal, S. Ali, and H. Susanto, “Pengujian Papan Komposit Diperkuat Serat Tandan Kosong Kelapa Sawit ( TKKS ) Dengan Menggunakan Alat Uji Impact Charpy,” Jurnal Mekanova : Mekanikal, Inovasi dan Teknologi, vol. 3, no. 1, Oct. 2017, doi: 10.35308/jmkn.v3i1.864.
I. P. Lokantara, “Analisis Kekuatan Impact Komposit Polyester-Serat Tapis Kelapa Dengan Variasi Panjang Dan Fraksi Volume Serat Yang Diberi Perlakuan NaOH,” Dinamika Teknik Mesin, vol. 2, no. 1, Jan. 2012 [Online]. Available: https://dinamika.unram.ac.id/index.php/DTM/article/view/111. [Accessed: Jan. 04, 2023] DOI: https://doi.org/10.29303/d.v2i1.111
E. Mahmuda, S. Savetlana, and Sugiyanto, “PENGARUH PANJANG SERAT TERHADAP KEKUATAN TARIK KOMPOSIT BERPENGUAT SERAT IJUK DENGAN MATRIK EPOXY,” Jurnal Ilmiah Teknik Mesin, vol. 1, no. 3, Jul. 2013.
M. Irsyad, N. Ir. , and A. Yulianto, “Sifat Fisis Dan Mekanis Pada Komposit Polyester Serat Batang Pisang Yang Disusun Asimetri [ 45o / -30o / 45o / -30o ],” Diploma Theses, Universitas Muhammadiyah Surakarta, 2015.
B. T. Mulyo and H. Yudiono, “ANALISIS KEKUATAN IMPAK PADA KOMPOSIT SERAT DAUN NANAS UNTUK BAHAN DASAR PEMBUATAN HELM SNI,” Jurnal Kompetensi Teknik, vol. 10, no. 2, pp. 1–8, 2018, doi: 10.15294/jkomtek.v10i2.16917.
F. Paundra, “ANALISIS KEKUATAN TARIK KOMPOSIT HYBRID BERPENGUAT SERAT BATANG PISANG KEPOK DAN SERAT PINANG,” Nozzle : Journal Mechanical Engineering, vol. 11, no. 1, pp. 9–13, Jan. 2022, doi: 10.30591/nozzle.v11i1.3122.
Y. Y. Pratama, R. H. Setyanto, and I. Priadythama, “PENGARUH PERLAKUAN ALKALI, FRAKSI VOLUME SERAT, DAN PANJANG SERAT TERHADAP KEKUATAN TARIK KOMPOSIT SERAT SABUT KELAPA - POLYESTER,” Jurnal Ilmiah Teknik Industri, vol. 13, no. 1, pp. 8–15, Jun. 2014, doi: https://doi.org/10.23917/jiti.v13i1.304.
W. W. Raharjo, D. Aries H, R. Fitriyan, and K. Indra. P, “Sifat Tarik dan Lentur Komposit rHDPE/Serat Cantula dengan Variasi Panjang Serat,” Proceeding Seminar Nasional Tahunan Teknik Mesin Indonesia XIV, Oct. 2015 [Online]. Available: https://repo-dosen.ulm.ac.id//handle/123456789/9081. [Accessed: Jan. 04, 2023]
M. E. Rahmasita, M. Farid, and H. Ardhyananta, “Analisa Morfologi Serat Tandan Kosong Kelapa Sawit Sebagai Bahan Penguat Komposit Absorpsi Suara,” Jurnal Teknik ITS, vol. 6, no. 2, pp. A787–A792, Oct. 2017, doi: 10.12962/j23373539.v6i2.24332. DOI: https://doi.org/10.12962/j23373539.v6i2.24332
O. Riza, S. Nikmatin, H. Hardhienata, and F. A. Syamani, “Analisa Sifat Mekanik pada Bahan Anti Peluru dari Adisi Berpenguat Serat Panjang Tandan Kosong Kelapa Sawit (TKKS),” NMJ, vol. 3, no. 1, pp. 24–32, May 2022, doi: 10.33369/nmj.v3i1.17567.
M. D. Rambe, T. B. Sitorus, H. Ambarita, F. H. Napitupulu, and Andianto P, “ANALISA MESIN PENDINGIN ADSORPSI DENGAN MENGGUNAKAN TENAGA MATAHARI,” Jurnal Dinamis, vol. 6, no. 4, 2018. DOI: https://doi.org/10.32734/dinamis.v6i4.7179
R. Rendy and S. Syahrizal, “Pengaruh Variasi Arah dan Massa Serat TKKS terhadap Kekuatan Material Komposit Termoset,” Jurnal Teknologi dan Rekayasa Manufaktur, vol. 4, no. 1, pp. 1–10, May 2022, doi: 10.48182/jtrm.v4i1.84. DOI: https://doi.org/10.48182/jtrm.v4i1.84
A. S. Jati, Y. E. Prawatya, and R. A. Wicaksono, “Karakterisasi Pengaruh Orientasi Serat Terhadap Sifat Fisis Komposit Serat Tandan Kosong Kelapa Sawit Dengan Perlakuan Alkali (NaOH),” JTRAIN: Jurnal Teknologi Rekayasa Teknik Mesin, vol. 2, no. 1, pp. 6–12, Dec. 2021.
N. H. Sari, A. Zainuri, and F. Wahyu, “Pengaruh Panjang Serat Dan Fraksi Volume Serat Pelepah Kelapa Terhadap Ketangguhan Impact Komposit Polyester,” DTM, vol. 1, no. 2, Jul. 2011. DOI: https://doi.org/10.29303/d.v1i2.120
R. K. Sinha, K. Sridhar, R. Purohit, and R. K. Malviya, “Effect of nano SiO2 on properties of natural fiber reinforced epoxy hybrid composite: A review,” Materials Today: Proceedings, vol. 26, pp. 3183–3186, 2020, doi: 10.1016/j.matpr.2020.02.657. [Online]. Available: https://linkinghub.elsevier.com/retrieve/pii/S2214785320314127. [Accessed: Jan. 04, 2023] DOI: https://doi.org/10.1016/j.matpr.2020.02.657
S. Sulaiman and A. Fauzan, “PENGARUH TEMPERATUR TEKAN PANAS PAPAN PARTIKEL BERBAHAN TANDAN KOSONG KELAPA SAWIT DAN KULIT KAYU PINUS TERHADAP SIFAT MEKANIK,” Jurnal Momentum, vol. 20, no. 2, pp. 128–132, doi: 10.21063/JM.2018.V20.2.128-132.
Copyright (c) 2023 Reksi Dwi Cahyanto, Agus Mujianto, Binyamin Binyamin, Andi Nugroho
This work is licensed under a Creative Commons Attribution 4.0 International License.