Oxy Acetylene Welding Analysis for Plastic Welding of Thermoplastic Polymer Materials


Analisa Las Oksi Asitilen untuk Las Plastik Material Polimer Termoplastik


  • (1) * Ayeik Abimanyu            Universitas Muhammadiyah Sidoarjo, Indonesia  
            Indonesia

  • (2)  Prantasi Harmi Tjahjanti            Universitas Muhammadiyah Sidoarjo, Indonesia  
            Indonesia

    (*) Corresponding Author

Abstract

Plastic welding technique is a technique of gluing to workpieces, especially plastic materials. The aim of this research was to join the thermoplastic polymer material using an acetylene oxy welding. The connection method is by melting the electrodes on the workpiece so that the electrodes can fuse to the parent material. The materials used are Polyethylene (PE), Polyvinyl chloride (PVC) and Polypropylene (PP) plastic sheets with the appropriate electrodes from their respective parents. After going through the welding process, the weld results are tested using a dye penetrant. The best results from the dye penetrant are then tested for hardness

Downloads

Download data is not yet available.

References

Agus Setiawan1), Y. S. (2011). Pengaruh Temperatur Pelat Landasan Selama Proses Friction Stir Welding Terhadap Kekuatan Tarik Sambungan Las Lembaran HDPE. Jurnal Rekayasa Mesin Vol.2, No. 3 Tahun 2011 : 232-240, 9.

Arie Indra Rusmana, S. (2018). MELAKUKAN PENETRANT TEST (PT) C.24LAS01.034.01 . jakarta selatan: DIREKTORAT JENDERAL PEMBINAAN PELATIHAN DAN PRODUKTIVITAS DIREKTORAT BINA STANDARDISASI KOMPETENSI DAN PELATIHAN KERJA .

Magdalena Feby Kumayasari, A. I. (2017). Studi Uji Kekerasan Rockwell Superficial VS Micro Vickers . JURNAL TEKNOLOGI PROSES DAN INOVASI INDUSTRI, 85-89.

Picture in here are illustration from public domain image (License) or provided by the author, as part of their works
Published
2021-03-28
 
How to Cite
[1]
Ayeik Abimanyu and Prantasi Harmi Tjahjanti, “Oxy Acetylene Welding Analysis for Plastic Welding of Thermoplastic Polymer Materials”, PELS, vol. 1, no. 1, Mar. 2021.